MECHANISM AND KINETIC PARAMETERS OF GAS CORROSION OF VT6 TITANIUM ALLOY IN CARBON TETRACHLORIDE
Abstract
Previously, the mechanism and kinetics of gas corrosion of commercially pure VT1-0 titanium in a carbon tetrachloride atmosphere and a temperature range of 573–773 K were studied. Using chemical reaction methods combined with X-ray phase analysis, it was found that at 673 K and above, the metal undergoes a constant transition to the gas phase as titanium tetrachloride during isothermal holding, and a porous, non-protective film of amorphous carbon forms on the sample.
About the Authors
V.F. Goryushkin
Siberian State Industrial University
Russian Federation
Russian Federation
Yu.V. Bendre
Siberian State Industrial University
S.A. Zentsova
Siberian State Industrial University
A.Yu. Gagarin
Siberian State Industrial University
References
1. Г о р ю ш к и н В.Ф., Б е н д р е Ю.В., Т о н к у ш и н Я.В., С о с к о в а Н.А., Б у - д о в с к и х Е.А. / Газовая коррозия титана в тетрахлориде углерода // Вестник Сибир- ского государственного индустриального университета. 2013. № 1(3). С. 25 – 28.
2. П о л м е а р Я. Легкие сплавы: от тради- ционных до нанокристаллов. – М.: Техно- сфера, 2008. – 464 с.
3. Л и д и н Р.А., М о л о ч к о В.А., А н д - р е е в а Л.Л. Реакции неорганических ве- ществ: справочник. 2-еизд., перераб. и доп. – М.: Дрофа, 2007. – 637 с.
4. Пат. 2422365 РФ. МПК CO1F 17/00. Устройство для получения безводных хлори- дов лантаноидов / Ю.В. Горюшкина, В.И. Ларин, В.Ф. Горюшкин. Заявл. 19.11.2009; опубл. 27.06.11. Бюл. № 18.
Review
For citations:
Goryushkin V., Bendre Yu., Zentsova S., Gagarin A. MECHANISM AND KINETIC PARAMETERS OF GAS CORROSION OF VT6 TITANIUM ALLOY IN CARBON TETRACHLORIDE. Bulletin of the Siberian State Industrial University. 2014;(2):40-43. (In Russ.)
Views:
2
Email this article 